TR – 60L
TR – 60LDESCRIPTION
Alumina based low cement content castable. Can be used as heavy duty material. It has low CaO content by the way is high strength material at medium temperature.
CHEMICAL ANALYSIS
Al 2 O 3: % 58 - 62Fe 2 O 3: % 2 – 2,4CaO: % 1,2 – 1,4PHYSICAL PROPERTIES
Grain Size: 0 - 5 mmMax. Service Temperature: 1600 o CWater Addition: % 8 – 9Bulk Density: 2,4 – 2,6 gr/cm 3SK (Refractoriness): 34 (1763 o C)Temperature
( o C)
Cold Crushing Strength
(kg/cm²)
Permanent Linear Change
(%)
Thermal Conductivity
(kcal/mh o C)
110
500
-
-
815
550
-
0,90
1100
620
-0,1
1,06
1400
680
-0,2
1,15
Tolerances are ± %5. ( Data is given after heating and cooling.)
PACKAGE
25 kg, in polyethylene or paper bags.
INSTALLATION
Cement and Lime Factories, petrochemical plants, reactors and vessels, steam generators, iron and steel industries.
-
TR – 75L
TR – 75LDESCRIPTION
Bauxite based Low-cement castable high strength against slag attacks. Because of low CaO content has high crushing strength and refractoriness.
CHEMICAL ANALYSIS
Al 2 O 3: % 74 – 76SiO 2: % 5 – 7CaO: % 1,6 – 1,8Fe 2 O 3: % 1,2 – 1,3PHYSICAL PROPERTIES
Grain Size: 0 - 5 mmMax. Service Temperature: 1680 o CWater Addition: % 6 – 8Bulk Density: 2,6 – 2,8 gr/cm 3Application: VibrationSK (Refractoriness): 38 (1850 o C)Temperature
( o C)
Cold Crushing Strength
(kg/cm²)
Permanent Linear Change
(%)
Thermal Conductivity
(kcal/mh o C)
110
550
-
-
1100
650
-0,20
1,05
1400
710
-0,30
1,20
Tolerances are ± %5. ( Data is given after heating and cooling.)
PACKAGE
25 kg, in polyethylene or paper bags.
INSTALLATION
Iron and steel industry, arc furnace, tundish, refinery and chemical plants.
-
TR – 85L
TR – 85LDESCRIPTION
High alumina based low-cement castable, high strength and slag attacks resistant used induction furnace spout and cover lining, arc furnace cover, tundish, ladle, non-ferrous melting furnace and transportation ladles, refinery, rotary kiln.
CHEMICAL ANALYSIS
Al 2 O 3: % 85 - 88CaO: % 1,4 – 1,6Fe 2 O 3: % 1,2 – 1,4PHYSICAL PROPERTIES
Grain Size: 0 - 5 mmMax. Service Temperature: 1750 o CWater Addition: % 6 – 8Bulk Density: 2,7 – 2,8 gr/cm 3Application: VibrationSK (Refractoriness): 39 (1880 o C)Temperature
( o C)
Cold Crushing Strength
(kg/cm²)
Permanent Linear Change
(%)
Thermal Conductivity
(kcal/mh o C)
110
620
-
-
1100
680
-0,20
1,10
1400
740
-0,30
1,30
Tolerances are ± %5. ( Data is given after heating and cooling.)
PACKAGE
25 kg, in polyethylene or paper bags.
INSTALLATION
Castable must be mixed in a clean vessel with 6-8 % water. For the right consistency makes ball in hand test. The mix must be flow 2-3mm between the fingers.. If it is possible the mix placed with vibration; if not by a wooden trowel. Make a hole in distance 10-15 cm with ø3mm bar for escape moisture.
-
TR – 95L
TR – 95LDESCRIPTION
Castable based on tabular alumina, resistant slag attacks and very high strengthened heavy-duty refractory material.
CHEMICAL ANALYSIS
Al 2 O 3: % 95 - 98CaO: % 1,2 – 1,4Fe 2 O 3: % 0,1 – 0,2PHYSICAL PROPERTIES
Grain Size: 0 - 5 mmMax. Service Temperature: 1850 o CWater Addition: % 6 – 8Bulk Density: 3,1 – 3,2 gr/cm 3Application: VibrationSK (Refractoriness): 41 (1960 o C)Temperature
( o C)
Cold Crushing Strength
(kg/cm²)
Permanent Linear Change
(%)
Thermal Conductivity
(kcal/mh o C)
110
650
-
-
1100
720
-0,20
1,20
1400
760
-0,30
1,30
Tolerances are ± %5. ( Data is given after heating and cooling.)
PACKAGE
25 kg, in polyethylene or paper bags.
INSTALLATION
Iron and steel industry; arc furnace cover, tundish, refinery, cement rotary kilns, chemical plants.